碳刨后的打磨要求是什么？

TIAN0412 · 发表于 2009-5-26 08:25

昨天，检查碳刨后的打前几天命令船厂刨开重新焊接的部位，发现焊道上有黑色的氧化皮和碳刨伤痕，那么碳刨后磨要求是什么？
必须全部打出金属本色吗？

小舢板2008 · 发表于 2009-5-26 08:41

应该是的吧！！

期待高人指点！！

学习中！！

plasma · 发表于 2009-5-26 08:44

Air carbon arc gouging uses an electric arc maintained between
a consumable carbon-graphite electrode and the material
surface to be gouged or cut. The arc produces a high
temperature which melts a portion of the surface of the underlying
material, while a high velocity air jet is directed at the
arc, blowing away the molten metal. If the process is not carried
out correctly carburised metal will re-solidify in the
groove, and carburisation of the wall of the groove occurs.
Since air carbon arc gouging often is done manually, it is difficult
to maintain optimum conditions, subsequent grinding to
remove carburised metal is therefore considered necessary.
For ferritic steels, a depth of 1.5 mm should be removed.

xuehu122 · 发表于 2009-5-26 08:46

应该是要打出金属本色，表面光洁

真☆100﹪♂ · 发表于 2009-5-26 09:19

不需要全部打出金属本色，只要把里面的氧化皮和杂质清理干净即可，简单的来回磨几下就可以了

chenhua19810927 · 发表于 2009-5-26 09:41

反面碳刨，要清根出白的

多多哥 · 发表于 2009-5-27 03:23

这个要看是什么位置的重要的板缝的碳刨后最好是打光亮只有打光亮后才看的到有没有缺陷什么的```````

为爱执着 · 发表于 2009-5-27 08:09

不一定要打出金属本色
但是把要上面的氧化物去掉

liuhongtao16 · 发表于 2009-5-27 13:56

理论露出金属光泽，碳刨后有渗碳层

coscowelder · 发表于 2009-5-28 21:13

海工碳刨后的打磨叫“出白” 可以理解然后还要根据母材性能确定打磨量

海上铁牛 · 发表于 2009-5-29 13:11

南方叫出白，北方叫清根，从焊工的角度讲清理干净就可以了，从船东的角度讲需要打磨干净。

chongming · 发表于 2009-5-29 13:45

打磨出金属本身，焊前清除垃圾

Nick12 · 发表于 2009-8-2 01:41

学习学习～这个还真不懂

PIN1323123 · 发表于 2009-8-2 07:34

同意楼上～～～～

kingzi1988 · 发表于 2009-8-2 08:18

不是打磨到没有裂纹和氧化皮就可以了吗

EAGLE鹰 · 发表于 2009-9-4 11:38

多谢指导！！

nell130026 · 发表于 2009-12-19 19:03

打磨要求就是：清根出白，主要是出白，意思很明白了，打磨光亮，还有就是焊缝缺陷肯定是不允许的

bingyu1986 · 发表于 2010-3-18 15:34

打磨渗碳层！

liushuyi6451 · 发表于 2010-6-6 12:44

船东要是严，不但要清根，还要抛光。

zfq2010 · 发表于 2010-6-6 14:23

9楼正确,关键是渗碳层